Měření tepelné vodivosti materiálů pro projekt MaMBA

Abstract

The content of this work is the measurement of thermal conductivity of materials within the MaMBA project. Single crystalline samples of LaNi$_5$ and PrNi$_5$ were successfully oriented along $a$ and $c$ axis each and disc-shaped polymer samples of PETG and PLA were 3D printed. Thermal conductivity was measured on these samples. The thermal conductivity electrical resistivity and Seebeck coefficient were measured on the intermetallic compounds in the temperature range 2-390K. A magnetoelastic interaction was observed in the PrNi$_5$ samples, contributing to the thermal conductivity. The magnetic character of the PrNi$_5$ compound also contributes to the resistivity at temperatures below 50K. This magnetic contribution was determined for both $a$ and $c$ axis. Finally, the temperature dependence of the thermal conductivity of PETG discs was measured in the temperature range 3-300K. The thermal conductivity of the PLA discs was measured at room temperature.

Náplní této práce je měření tepelné vodivosti materiálů v rámci projektu MaMBA. Byly uspěšně připraveny monokrystalické vzorky PrNi$_5$ a LaNi$_5$ podél os $a$ a $c$ a vytištěny polymerové vzorky ve tvaru disku z polymerů PETG a PLA. Na těchto vzorcích byla měřena tepelná vodivost. Na intermetalických sloučeninách byly změřeny teplotní vodivost, měrný elektrický odpor a Seebeckův koeficient na teplotním intervalu 2-390K. Byla pozorována magnetoelastická interakce ve vzorcích PrNi$_5$, přispívající k tepelné vodivosti. Magnetický charakter sloučeniny PrNi$_5$ přispívá také k měrnému elektrickému odporu při teplotách pod 50K. Tento magnetický příspěvek byl určen pro obě osy $a$ a $c$. Nakonec byla změřena teplotní závislost tepelné vodivosti disků PETG na teplotním intervalu 3-300K. Tepelná vodivost disků PLA byla změřena při pokojové teplotě.