Mapping of changes in optical and magneto-optical responses of Ni-Mn-Ga thin films across martensitic transformation and strain relaxation

Abstract

This thesis studies optical and magneto-optical responses of thin epitaxial Ni-Mn- Ga films prepared by magnetron sputtering. The relative permittivity tensor spectra were computed from the spectroscopic ellipsometry data measured both without the external magnetic field and in the out-of-plane magnetic field configuration. For one of the thin film samples, measurements across martensitic transformation were performed and temperature-hysteresis was observed. The analysis of the obtained spectra for thickness- varied series of samples clearly demonstrated the influence of substrate-induced strain and revealed a strong correlation between the out-of-plane lattice parameter and the properties of the obtained spectra. 1

Tato diplomová práce se zabývá studiem optické a magnetooptické odezvy tenkých epitaxních vrstev Ni-Mn-Ga, které byly připraveny pomocí magnetronového naprašování. Byl proveden výpočet spekter tenzoru relativní permitivity na základě elipsometrických dat získaných z měření bez přítomnosti magnetického pole a měření s magnetickým polem v polární konfiguraci. Pro jednen ze vzorků tenkých vrstev byla provedena série měření napříč martensitickou transformací a bylo pozorováno hysterezní chování. Analýza získa- ných spekter pro sérii vzorků s různou tloušťkou jasně demonstrovala vliv pnutí, které je způsobeno substrátem, a ukázala silnou korelaci mezi mřížovým parameterem v kolmém směru vůči povrchu a vlastnostmi získaných spekter. 1